三沙市电工钢出口27QG095

电工钢硅钢片Electrical steel, also known as silicon steel sheet, is an indispensable metal material in the power, electronics, and military industries, and is also the largest functional material in production. It is mainly used as the iron core for various motors, generators, and transformers. Specific total loss (iron loss) is the total power consumed per unit mass of material when the magnetic polarization waveform remains sinusoidal, with a specific peak and frequency. The specific total loss is represented by the symbol P (Jm/f), in W/kg. Example: P1.5/50 represents the specific total loss at a maximum magnetic polarization intensity of 1.5T and a frequency of 50Hz. 3.2 Magnetic Polarization Q/BQB 480-20212 Magnetic polarization intensity refers to the peak magnetic polarization intensity of a specific magnetic field intensity when a sample is subjected to alternating magnetization. Its symbol is J (H), and the unit is T (Tesla). Example: J5000 represents the peak magnetic polarization intensity corresponding to a magnetic field intensity peak of 5000A/m. The material grades in this document are classified based on the nominal maximum specific total loss P1.5/50 (W/kg) at a magnetic polarization strength of 1.5T and a frequency of 50Hz, as well as the nominal thickness of the material. They are further divided into three categories based on product characteristics: ordinary type, stress relief annealing type, and high-efficiency type. Example 1: B35A210 represents a common non oriented electrical steel with a nominal thickness of 0.35mm, and the maximum nominal specific total loss value P1.5/50 is 2.10W/kg； Example 2: B35AR300 represents a stress relieved annealed non oriented electrical steel with a nominal thickness of 0.35mm, and the maximum nominal specific total loss value P1.5/50 is 3.00W/kg； Example 3: B35AH230 represents an efficient non oriented electrical steel with a nominal thickness of 0.35mm, and the maximum nominal specific loss value P1.5/50 is 2.30W/kg. Example 4: 35WW210 represents a normal type WW non oriented electrical steel with a nominal thickness of 0.35mm, and the maximum nominal specific loss value P1.5/50 is 2.10W/kg. Example 5: 35WH230 represents an efficient WH non oriented electrical steel with a nominal thickness of 0.35mm, and the maximum nominal specific loss value P1.5/50 is 2.30W/kg. The classification and code of insulation coatings shall comply with the provisions of Table 2. Table 2 Classification and Code of Insulation Coatings Type Code Characteristics of Insulation Coatings Semi organic Thin Coating A Improves Punching Performance and Has Good Weldability Semi organic Thick Coating H has Good Punching Performance and High Interlayer Resistance Semi organic Chromium Free Thin Coating K does not contain chromium and has good weldability Semi organic Chromium Free Thick Coating M does not contain chromium and has good insulation performance Semi organic Chromium Free Extreme Thick Coating J does not contain chromium and has excellent insulation performance Semi organic Chromium Free Ultra Thick Coating L does not contain chromium and has extremely high insulation performance Self adhesive Coating

电工钢硅钢片：本文件的符号和相应的说明见表1。表 1 符号和说明符号 单位 说明P W/kg 比总损耗，通常称为铁损P1.5/50 W/kg 磁极化强度在1.5T、安徽亳州附近频率在50Hz下测得的比总损耗P1 W/kg 横向试样的比总损耗值P1.5/50 P2 W/kg 纵向试样的比总损耗值P1.5/50 T1.5/50 ％ 比总损耗P1.5/50的各向异性H A/m 磁场强度J T 磁极化强度J1000 T 磁场强度峰值为1000A/m下测得的磁极化强度峰值J2500 T 磁场强度峰值为2500A/m下测得的磁极化强度峰值J5000 T 磁场强度峰值为5000A/m下测得的磁极化强度峰值J10000 T 磁场强度峰值为10000A/m下测得的磁极化强度峰值μ0 H/m 真空中的磁导率取4?×10-7 B T 磁感应强度，B＝μ0H＋JReL MPa 下屈服强度Rm MPa 抗拉强度A ％ 断后伸长率C Ω·cm2/面或Ω·mm2/面 表面绝缘电阻系数RA Ω·cm2/片或Ω·mm2/片 层间电阻系数