表面化学性质
The two is to look at the honeycomb activated carbon products produced by the bubble, if the bubble is more the better the quality of the product. We can do a little experiment, a handful of honeycomb activated carbon products into the water, because the water penetration effect, water will be immersed in the pores of activated carbon, so the pore in the air, resulting in a series of very small bubbles, pulled out a tiny bubbles lines in the water, at the same time also issued Zizi bubble sound, looked very interesting. If this phenomenon is very serious, and the longer the duration, then it is proved that the honeycomb activated carbon product pore structure is very developed, that is, the better adsorption performance of honeycomb activated carbon.
| 主要成分 | 活性炭 | 正常抗压 | 大于0.8mpa | |
| 常用规格 | 50*50*100mm、100*100*100mm | 使用温度 | 小于400摄氏度 | |
| 孔密度 | 100孔/平方英寸、150孔/平方英寸 | 空塔风速 | 0.8米/秒 | |
| 比表面积 | 大于700平方/克 | 外观 | 产品表面平整，没有裂纹 | |
|
| ||||
| 项目 | Sub ject | 指标 | Index | |
| 规格 | Specification(mm) | 50*50*100 100*100*1000 | ||
| 碘吸附值 | Iodine Absorb(mg/g) | 》950 | ||
| 比表面积 | Specific Surface Area(m2/g) | 》1050 | ||
| 四氯化碳 | CTC(%) | 》65 | ||
| 抗压强度 | Compressive strebgth(mpa) | 0.9 | ||
| 水份 | Moisture(%） | 《5 | ||
| 方孔 | Square hole(in)2 | 150 | ||
| 壁厚 | Wall thickness(mm) | 1 | ||
| 使用温度 | Temperature(℃） | 》400 | ||
| 体积温度 | Bulk Density g/cm3 | 0.35-0.60 | ||
| 苯吸附率 | Adsorption rate of benzene % | 动态吸附》37 | ||
| 苯吸附率 | Adsorption rate of benzene % | 静态吸附》52 | ||
| 主要成分 | 活性炭 | 正常抗压 | 大于0.8mpa | |
| 常用规格 | 50*50*100mm、100*100*100mm | 使用温度 | 小于400摄氏度 | |
| 孔密度 | 100孔/平方英寸、150孔/平方英寸 | 空塔风速 | 0.8米/秒 | |
| 比表面积 | 大于700平方/克 | 外观 | 产品表面平整，没有裂纹 | |
|
| ||||
| 项目 | Sub ject | 指标 | Index | |
| 规格 | Specification(mm) | 50*50*100 100*100*1000 | ||
| 碘吸附值 | Iodine Absorb(mg/g) | 》950 | ||
| 比表面积 | Specific Surface Area(m2/g) | 》1050 | ||
| 四氯化碳 | CTC(%) | 》65 | ||
| 抗压强度 | Compressive strebgth(mpa) | 0.9 | ||
| 水份 | Moisture(%） | 《5 | ||
| 方孔 | Square hole(in)2 | 150 | ||
| 壁厚 | Wall thickness(mm) | 1 | ||
| 使用温度 | Temperature(℃） | 》400 | ||
| 体积温度 | Bulk Density g/cm3 | 0.35-0.60 | ||
| 苯吸附率 | Adsorption rate of benzene % | 动态吸附》37 | ||
| 苯吸附率 | Adsorption rate of benzene % | 静态吸附》52 | ||
| 主要成分 | 活性炭 | 正常抗压 | 大于0.8mpa | |
| 常用规格 | 50*50*100mm、100*100*100mm | 使用温度 | 小于400摄氏度 | |
| 孔密度 | 100孔/平方英寸、150孔/平方英寸 | 空塔风速 | 0.8米/秒 | |
| 比表面积 | 大于700平方/克 | 外观 | 产品表面平整，没有裂纹 | |
|
| ||||
| 项目 | Sub ject | 指标 | Index | |
| 规格 | Specification(mm) | 50*50*100 100*100*1000 | ||
| 碘吸附值 | Iodine Absorb(mg/g) | 》950 | ||
| 比表面积 | Specific Surface Area(m2/g) | 》1050 | ||
| 四氯化碳 | CTC(%) | 》65 | ||
| 抗压强度 | Compressive strebgth(mpa) | 0.9 | ||
| 水份 | Moisture(%） | 《5 | ||
| 方孔 | Square hole(in)2 | 150 | ||
| 壁厚 | Wall thickness(mm) | 1 | ||
| 使用温度 | Temperature(℃） | 》400 | ||
| 体积温度 | Bulk Density g/cm3 | 0.35-0.60 | ||
| 苯吸附率 | Adsorption rate of benzene % | 动态吸附》37 | ||
| 苯吸附率 | Adsorption rate of benzene % | 静态吸附》52 | ||
| 主要成分 | 活性炭 | 正常抗压 | 大于0.8mpa | |
| 常用规格 | 50*50*100mm、100*100*100mm | 使用温度 | 小于400摄氏度 | |
| 孔密度 | 100孔/平方英寸、150孔/平方英寸 | 空塔风速 | 0.8米/秒 | |
| 比表面积 | 大于700平方/克 | 外观 | 产品表面平整，没有裂纹 | |
|
| ||||
| 项目 | Sub ject | 指标 | Index | |
| 规格 | Specification(mm) | 50*50*100 100*100*1000 | ||
| 碘吸附值 | Iodine Absorb(mg/g) | 》950 | ||
| 比表面积 | Specific Surface Area(m2/g) | 》1050 | ||
| 四氯化碳 | CTC(%) | 》65 | ||
| 抗压强度 | Compressive strebgth(mpa) | 0.9 | ||
| 水份 | Moisture(%） | 《5 | ||
| 方孔 | Square hole(in)2 | 150 | ||
| 壁厚 | Wall thickness(mm) | 1 | ||
| 使用温度 | Temperature(℃） | 》400 | ||
| 体积温度 | Bulk Density g/cm3 | 0.35-0.60 | ||
| 苯吸附率 | Adsorption rate of benzene % | 动态吸附》37 | ||
| 苯吸附率 | Adsorption rate of benzene % | 静态吸附》52 | ||
普邦环保材料有限公司是一家全国专业销售 湖南湘西碳酸氢钠的供应商，投资总金额5000万，是一家集生产，加工，销售为一体的大型 湖南湘西碳酸氢钠公司。公司主要经营销售 湖南湘西碳酸氢钠。公司利用 周边良好的物流关系，为客户快捷，的铁路，汽运，快运等运输方式。普邦环保材料有限公司业以自身的努力和实践行动回报社会。有口皆碑的信誉、精益求精的产品和力求完美的服务是普邦环保材料有限公司成功的关键所在,本着 “客户di yi、技术di yi、质量di yi、服务di yi”的原则，公司力求创造良好业绩。 本着造福社会，服务社会的企业理念，致力于全国模具业的发展。
活化是在有氧化剂的作用下，对碳化后的材料加热，以生产活性炭产品。当氧化过程的温度在800-900℃时，一般用蒸汽或二氧化碳为氧化剂;当氧化温度在600℃以下时，一般用空气做氧化剂。对于活化过程所起的作用，目前只有大致的理解。在活化过程中，烧掉了碳化时吸附的碳氢化合物，把原有空隙边上的碳氢原子烧掉，起了扩大孔隙的作用，并把孔隙与孔隙之间烧穿。活化使活性炭变成一种良好的多孔结构，碳化及活化后的晶体片状结。